EFFECT OF SURFACE FINISH ON THE TENSILE BEHAVIOR OF DACRON© 360 WOVEN

In the present paper some experimental analyses effected on Dacron© 360 woven with and without surface treatment, aimed to characterize the effect of this treatment on the constitutive behavior, are presented. This woven, widely adopted in sail manufacturing, is obtained by weaving polyethylene terephthalate (PET) yarn and it shows some peculiar features due to the manufacturing process. The experimental tests, in terms of tensile tests, clearly show the orthotropy features of the material and the effect of the treatment which results in a stiffer behavior especially along the warp and bias direction and in an increment of ultimate strength in all directions.

Nel presente lavoro vengono presentate alcune indagini sperimentali mirate alla caratterizzazione dell’effetto del trattamento superficiale sul comportamento costitutivo di un tessuto in Dacron© 360. Tale tessuto, largamente utilizzato nella realizzazione di vele, è ottenuto dalla tessitura di fili di polietilene tereftalato (PET) e presenta alcune peculiarità dovute al processo manifatturiero. Le prove di trazione realizzate evidenziano le caratteristiche di ortotropia del materiale e l’effetto del trattamento superficiale che si manifesta principalmente in un comportamento più rigido nella direzione dell’ordito ed in quella inclinata e in un aumento della resistenza ultima in tutte le direzioni.