Superhydrophobic coatings were fabricated through a one-step electrochemical process onto the surface of 316L stainless steel samples. The presence of hierarchical structures at micro/ nanoscale and manganese stearate into the coatings gave superhydrophobicity to the coating, with contact angle of ~160◦, and self-cleaning ability. Corrosion resistance of 316L samples was also assessed also after the electrodeposition process through Electrochemical Impedance Spectra recorded in an aqueous solution mimicking seawater condition.
Zaffora A., Di Franco F., Megna B., Santamaria M. (2021). One-step electrodeposition of superhydrophobic coating on 316L stainless steel. METALS, 11(11) [10.3390/met11111867].
One-step electrodeposition of superhydrophobic coating on 316L stainless steel
Zaffora A.;Di Franco F.
;Megna B.;Santamaria M.
2021-11-20
Abstract
Superhydrophobic coatings were fabricated through a one-step electrochemical process onto the surface of 316L stainless steel samples. The presence of hierarchical structures at micro/ nanoscale and manganese stearate into the coatings gave superhydrophobicity to the coating, with contact angle of ~160◦, and self-cleaning ability. Corrosion resistance of 316L samples was also assessed also after the electrodeposition process through Electrochemical Impedance Spectra recorded in an aqueous solution mimicking seawater condition.File | Dimensione | Formato | |
---|---|---|---|
2021_Metals_Superhydro-316L-SS.pdf
accesso aperto
Tipologia:
Versione Editoriale
Dimensione
2.91 MB
Formato
Adobe PDF
|
2.91 MB | Adobe PDF | Visualizza/Apri |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.