Aim of the present paper is to evaluate how the bearing behavior of pinned flax composites can be influenced by their exposition to critical environment such as marine one. To this scope, flax fibers/epoxy pinned laminate was exposed up to 60 days to salt-fog environment, according to ASTM B 117 standard. In particular, samples having different hole diameter (D), laminate width (W), and hole center to laminate free edge distance (E) have been tested under single lap bearing tests at varying the aging exposition time. Following this procedure, an experimental 2D failure map clustering main failure modes was created by placing the experimental results in the plane E/D versus W/D ratios, and its variation was analyzed at varying the aging exposition. Experimental results showed that environmental aging induced modification on the mechanical performances of the pinned composite. Furthermore, the failure map, defined by E/D and W/D ratios axes, evidenced a progressive modification of damage mechanisms transitions, at increasing the exposition time. In particular, due to significant reductions of tensile and shear strengths of flax laminate, the progressive fracture by bearing mode was not observed for aged samples, replaced by premature and catastrophic shear out and net tension mechanisms.

Fiore V., Calabrese L., Scalici T., Valenza A. (2020). Evolution of the bearing failure map of pinned flax composite laminates aged in marine environment. COMPOSITES. PART B, ENGINEERING, 187 [10.1016/j.compositesb.2020.107864].

Evolution of the bearing failure map of pinned flax composite laminates aged in marine environment

Fiore V.
;
Valenza A.
2020-01-01

Abstract

Aim of the present paper is to evaluate how the bearing behavior of pinned flax composites can be influenced by their exposition to critical environment such as marine one. To this scope, flax fibers/epoxy pinned laminate was exposed up to 60 days to salt-fog environment, according to ASTM B 117 standard. In particular, samples having different hole diameter (D), laminate width (W), and hole center to laminate free edge distance (E) have been tested under single lap bearing tests at varying the aging exposition time. Following this procedure, an experimental 2D failure map clustering main failure modes was created by placing the experimental results in the plane E/D versus W/D ratios, and its variation was analyzed at varying the aging exposition. Experimental results showed that environmental aging induced modification on the mechanical performances of the pinned composite. Furthermore, the failure map, defined by E/D and W/D ratios axes, evidenced a progressive modification of damage mechanisms transitions, at increasing the exposition time. In particular, due to significant reductions of tensile and shear strengths of flax laminate, the progressive fracture by bearing mode was not observed for aged samples, replaced by premature and catastrophic shear out and net tension mechanisms.
2020
Fiore V., Calabrese L., Scalici T., Valenza A. (2020). Evolution of the bearing failure map of pinned flax composite laminates aged in marine environment. COMPOSITES. PART B, ENGINEERING, 187 [10.1016/j.compositesb.2020.107864].
File in questo prodotto:
File Dimensione Formato  
Post-print_JCOMB_107864.pdf

accesso aperto

Tipologia: Post-print
Dimensione 4.61 MB
Formato Adobe PDF
4.61 MB Adobe PDF Visualizza/Apri
1-s2.0-S135983681931220X-main.pdf

Solo gestori archvio

Tipologia: Versione Editoriale
Dimensione 2.21 MB
Formato Adobe PDF
2.21 MB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10447/398760
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 29
  • ???jsp.display-item.citation.isi??? 22
social impact