This in vitro study evaluated the marginal microleakage of composite inlays luted with 3 different cement systems. The null hypothesis was that the luting materials would not influence dye penetration, showing the same degree of microleakage. Thirty-six sound molars were selected, mesio-occlusodistal cavities were prepared, and the teeth were randomly divided into 3 groups (n = 12). Composite resin inlay restorations were made and cemented using a dual-curing resin cement (Calibra), a light-curing flowable composite (Charisma Flow), or a self-adhesive resin cement (RelyX Unicem). The restored teeth were subjected to fatigue cycles and immersed in 0.5% basic fuchsin dye for 24 hours. Two orthogonal cuts were made to enable evaluation of dye penetration at the cervical and occlusal margins. The sections were evaluated with a 4-point scale ranging from 0 (no penetration) to 3 (penetration up to the cavity floor [occlusal margins] or axial wall [cervical margins]). The Calibra and Charisma Flow groups showed greater microleakage, notably at the cervical margins, whereas RelyX Unicem specimens showed the least dye penetration. Significant differences were found between the Calibra and Charisma Flow groups and between the Charisma Flow and RelyX Unicem groups (P < 0.05). No statistically significant differences were detected between the Calibra and RelyX Unicem groups. The microleakage associated with the flowable composite was significantly greater than that associated with both resin cements, results that discourage its use for luting of Class II composite inlays.

Melilli, D., Cumbo, E.M., Baldissara, P., Wandscher, V.F., Valandro, L.F., Gallina, G., et al. (2018). Evaluation of marginal leakage after mechanical fatigue cycling of composite inlays luted with different cements. GENERAL DENTISTRY, 66(4), 51-55.

Evaluation of marginal leakage after mechanical fatigue cycling of composite inlays luted with different cements

Melilli, Dario;Cumbo, Enzo Maria;Gallina, Giuseppe;Pizzo, Giuseppe
2018-01-01

Abstract

This in vitro study evaluated the marginal microleakage of composite inlays luted with 3 different cement systems. The null hypothesis was that the luting materials would not influence dye penetration, showing the same degree of microleakage. Thirty-six sound molars were selected, mesio-occlusodistal cavities were prepared, and the teeth were randomly divided into 3 groups (n = 12). Composite resin inlay restorations were made and cemented using a dual-curing resin cement (Calibra), a light-curing flowable composite (Charisma Flow), or a self-adhesive resin cement (RelyX Unicem). The restored teeth were subjected to fatigue cycles and immersed in 0.5% basic fuchsin dye for 24 hours. Two orthogonal cuts were made to enable evaluation of dye penetration at the cervical and occlusal margins. The sections were evaluated with a 4-point scale ranging from 0 (no penetration) to 3 (penetration up to the cavity floor [occlusal margins] or axial wall [cervical margins]). The Calibra and Charisma Flow groups showed greater microleakage, notably at the cervical margins, whereas RelyX Unicem specimens showed the least dye penetration. Significant differences were found between the Calibra and Charisma Flow groups and between the Charisma Flow and RelyX Unicem groups (P < 0.05). No statistically significant differences were detected between the Calibra and RelyX Unicem groups. The microleakage associated with the flowable composite was significantly greater than that associated with both resin cements, results that discourage its use for luting of Class II composite inlays.
2018
Melilli, D., Cumbo, E.M., Baldissara, P., Wandscher, V.F., Valandro, L.F., Gallina, G., et al. (2018). Evaluation of marginal leakage after mechanical fatigue cycling of composite inlays luted with different cements. GENERAL DENTISTRY, 66(4), 51-55.
File in questo prodotto:
File Dimensione Formato  
General Dentistry 2018.pdf

Solo gestori archvio

Descrizione: articolo principale
Dimensione 622.11 kB
Formato Adobe PDF
622.11 kB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10447/293130
Citazioni
  • ???jsp.display-item.citation.pmc??? 1
  • Scopus 4
  • ???jsp.display-item.citation.isi??? ND
social impact