We report a novel multi-step method for the preparation of ordered mesoporous titania scaffolds and show an illustrative example of their application to solar cells. The method is based on (monolayer) colloidal nanosphere lithography that makes use of polystyrene nanoparticles organised at a water–air interface and subsequently transferred onto a solid substrate. A titania precursor solution (titanium(IV) isopropoxide in ethanol) is then drop-cast onto the monolayer and left to “incubate” overnight. Surprisingly, instead of the expected inverse monolayer-structure, a subsequent calcination step of the precursor yields an ordered monolayer of hollow titania nanospheres with a wall thickness of ∼30–50 nm, and a slightly larger diameter than that of the starting spheres. X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) characterization of such scaffolds confirm that they consist of nanocrystalline anatase titania, and that any polystyrene/carbon residues in the scaffolds are below the XPS detection level. As an illustrative application we prepared perovskite solar cells incorporating the templated-nanoparticle scaffolds displaying a respectable power conversion efficiency of ∼9%, twice as large as that of our unoptimized “reference” cells (i.e. incorporating conventional mesoporous or compact titania scaffolds), thereby also demonstrating that the process is relatively robust with respect to optimization of the process parameters.

Robbiano, V., Paternò, G.M., Cotella, G.F., Fiore, T., Dianetti, M., Scopelliti, M., et al. (2018). Polystyrene nanoparticle-templated hollow titania nanosphere monolayers as ordered scaffolds. JOURNAL OF MATERIALS CHEMISTRY. C, 6, 2502-2508 [10.1039/c7tc04070a].

Polystyrene nanoparticle-templated hollow titania nanosphere monolayers as ordered scaffolds

Fiore, T.;Scopelliti, M.;Pignataro, B.;
2018-01-01

Abstract

We report a novel multi-step method for the preparation of ordered mesoporous titania scaffolds and show an illustrative example of their application to solar cells. The method is based on (monolayer) colloidal nanosphere lithography that makes use of polystyrene nanoparticles organised at a water–air interface and subsequently transferred onto a solid substrate. A titania precursor solution (titanium(IV) isopropoxide in ethanol) is then drop-cast onto the monolayer and left to “incubate” overnight. Surprisingly, instead of the expected inverse monolayer-structure, a subsequent calcination step of the precursor yields an ordered monolayer of hollow titania nanospheres with a wall thickness of ∼30–50 nm, and a slightly larger diameter than that of the starting spheres. X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) characterization of such scaffolds confirm that they consist of nanocrystalline anatase titania, and that any polystyrene/carbon residues in the scaffolds are below the XPS detection level. As an illustrative application we prepared perovskite solar cells incorporating the templated-nanoparticle scaffolds displaying a respectable power conversion efficiency of ∼9%, twice as large as that of our unoptimized “reference” cells (i.e. incorporating conventional mesoporous or compact titania scaffolds), thereby also demonstrating that the process is relatively robust with respect to optimization of the process parameters.
2018
Robbiano, V., Paternò, G.M., Cotella, G.F., Fiore, T., Dianetti, M., Scopelliti, M., et al. (2018). Polystyrene nanoparticle-templated hollow titania nanosphere monolayers as ordered scaffolds. JOURNAL OF MATERIALS CHEMISTRY. C, 6, 2502-2508 [10.1039/c7tc04070a].
File in questo prodotto:
File Dimensione Formato  
c7tc04070a1.pdf

accesso aperto

Descrizione: supplementary info
Tipologia: Altro materiale (es. dati della ricerca)
Dimensione 3.7 MB
Formato Adobe PDF
3.7 MB Adobe PDF Visualizza/Apri
c7tc04070a.pdf

accesso aperto

Descrizione: Articolo
Tipologia: Versione Editoriale
Dimensione 2.44 MB
Formato Adobe PDF
2.44 MB Adobe PDF Visualizza/Apri

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/10447/277555
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 18
  • ???jsp.display-item.citation.isi??? 17
social impact