IRIS è il sistema di gestione integrata dei dati della ricerca (persone, pubblicazioni, progetti, attività) adottato dall’Università di Palermo, e ha lo scopo di raccogliere, conservare, documentare, e diffondere ad accesso aperto le informazioni relative alla produzione scientifica degli autori afferenti all’Ateneo.
EnglishThe bioadhesive properties of a novel chemical hydrogel based on a polymer of protein-like structure, have been investigated by using ATR FT-IR spectroscopy. In particular, the copolymer PHG obtained by partial derivatization of PHEA with GMA was chemically crosslinked by UVirradiation at 313 nm. Crosslinked PHG was treated with water to obtain a swelled sample, named PHG-UV gel, that was brought into contact with a phosphate buffer/citric acid solution at pH 7.0 in the absence or in the presence of mucin at various concentrations (0.01, 0.1 and 1 wt.-%). Preliminary dynamic swelling studies have evidenced the occurrence of an interaction between thePHG-UVgel and the glycoprotein. This result was confirmed by ATR FT-IR measurements. A diffusion model using a solution of Ficks’ second law was employed to determine the diffusion coefficient of water into PHG-UV gel as a consequence of adsorption and/or interdiffusion which occur at the PHG-UV gel/mucin solution interface. Experimental results suggest a potential use of PHG-UV gel to prepare bioadhesive devices.
Saiano, F., Pitarresi, G., Mandracchia, D., & Giammona, G. (2005). BIOADHESIVE PROPERTIES OF A POLYAMINOACIDIC HYDROGEL: EVALUATION BY ATR FT-IR SPECTROSCOPY. MACROMOLECULAR BIOSCIENCE, 5(7), 653-661.
| Data di pubblicazione: | 2005 | |
| Titolo: | BIOADHESIVE PROPERTIES OF A POLYAMINOACIDIC HYDROGEL: EVALUATION BY ATR FT-IR SPECTROSCOPY | |
| Autori: | ||
| Citazione: | Saiano, F., Pitarresi, G., Mandracchia, D., & Giammona, G. (2005). BIOADHESIVE PROPERTIES OF A POLYAMINOACIDIC HYDROGEL: EVALUATION BY ATR FT-IR SPECTROSCOPY. MACROMOLECULAR BIOSCIENCE, 5(7), 653-661. | |
| Rivista: | ||
| Abstract: | The bioadhesive properties of a novel chemical hydrogel based on a polymer of protein-like structure, have been investigated by using ATR FT-IR spectroscopy. In particular, the copolymer PHG obtained by partial derivatization of PHEA with GMA was chemically crosslinked by UVirradiation at 313 nm. Crosslinked PHG was treated with water to obtain a swelled sample, named PHG-UV gel, that was brought into contact with a phosphate buffer/citric acid solution at pH 7.0 in the absence or in the presence of mucin at various concentrations (0.01, 0.1 and 1 wt.-%). Preliminary dynamic swelling studies have evidenced the occurrence of an interaction between thePHG-UVgel and the glycoprotein. This result was confirmed by ATR FT-IR measurements. A diffusion model using a solution of Ficks’ second law was employed to determine the diffusion coefficient of water into PHG-UV gel as a consequence of adsorption and/or interdiffusion which occur at the PHG-UV gel/mucin solution interface. Experimental results suggest a potential use of PHG-UV gel to prepare bioadhesive devices. | |