Among transparent electrodes, transparent conductive oxides (TCO)/metal/TCO structures can achieve optical and electrical performances comparable to, or better than, single TCO layers and very thin metallic films. In this work, we report on thin multilayers based on aluminum zinc oxide (AZO), indium tin oxide (ITO) and Ag deposited by RF magnetron sputtering on soda lime glass at room temperature. The TCO/Ag/TCO structures with thicknesses of about 50/10/50 nm were deposited with all combinations of AZO and ITO as top and bottom layers. While the electrical conductivity is dominated by the Ag intralayer irrespective of the TCO nature, the optical transmissions show a dependence on the nature of the top and bottom TCOs, mainly due to the change in the reflectivity of the multilayers. Structural, electrical and optical properties are studied to optimize the structure for very thin transparent electrodes suitable for photovoltaic applications. © 2014 Springer-Verlag Berlin Heidelberg.
Boscarino, S., Crupi, I., Mirabella, S., Simone, F., Terrasi, A. (2014). TCO/Ag/TCO transparent electrodes for solar cells application. APPLIED PHYSICS. A, MATERIALS SCIENCE & PROCESSING, 116(3), 1287-1291 [10.1007/s00339-014-8222-9].
TCO/Ag/TCO transparent electrodes for solar cells application
crupi, Isodiana;
2014-01-01
Abstract
Among transparent electrodes, transparent conductive oxides (TCO)/metal/TCO structures can achieve optical and electrical performances comparable to, or better than, single TCO layers and very thin metallic films. In this work, we report on thin multilayers based on aluminum zinc oxide (AZO), indium tin oxide (ITO) and Ag deposited by RF magnetron sputtering on soda lime glass at room temperature. The TCO/Ag/TCO structures with thicknesses of about 50/10/50 nm were deposited with all combinations of AZO and ITO as top and bottom layers. While the electrical conductivity is dominated by the Ag intralayer irrespective of the TCO nature, the optical transmissions show a dependence on the nature of the top and bottom TCOs, mainly due to the change in the reflectivity of the multilayers. Structural, electrical and optical properties are studied to optimize the structure for very thin transparent electrodes suitable for photovoltaic applications. © 2014 Springer-Verlag Berlin Heidelberg.File | Dimensione | Formato | |
---|---|---|---|
APA Boscarino.pdf
Solo gestori archvio
Dimensione
523.95 kB
Formato
Adobe PDF
|
523.95 kB | Adobe PDF | Visualizza/Apri Richiedi una copia |
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.