Structural Characterization of Surfactant-Coated Bimetallic Cobalt/Nickel Nanoclusters by XPS, EXAFS, WAXS, and SAXS

Cobalt nickel bimetallic nanoparticles were synthesized by changing the sequence of the chemical reduction of Co(II) and Ni(II) ions confined in the core of bis(2-ethylhexyl)phosphate (2)., and Ni(DEHP)(2). The reduction was carried out by mixing, sequentially or contemporaneously, fixed amounts of n-heptane solution of Co(DEHP)2 and Ni(DEHP)2 micelles with a solution of sodium borohydride in ethanol at a fixed (reductant)/(total metal) molar ratio. This procedure involves the rapid formation of surfactant-coated nanoparticles, indicated as Co/Ni (Co after Ni), Ni/Co (Ni after Co), and Co + Ni (simultaneous), followed by their slow separation as nanostructures embedded in a sodium bis(2-ethylhexyl)phosphate matrix. The resulting composites, together with those obtained by reducing the n-heptane solutions of pure Co(DEHP)(2) or Ni(DEHP)(2), were characterized by XPS, EXAFS, WAXS, and SAXS. The data analysis confirms the presence of nanometer-sized surfactant-coated cobalt, nickel, and cobalt/nickel particles. As expected, the composition and internal structure of cobalt/nickel bimetallic nanoparticles are influenced by the preparation sequence as well as by the "chemical affinity" between the surfactant and the metal. However, some atomic-scale physicochemical processes play a subtle role in determining the structural features of bimetallic nanoparticles. Further effects due to the competition between nanoparticle growing process and surfactant adsorption at the nanoparticle surface were observed.